| 沈湘凌,陈广杰,郭大亮,李静,童欣.MXene/CNF复合气凝胶的制备及其湿敏性能研究[J].中国造纸,2024,43(8):1-11 |
二维码（扫一下试试看！） |
| MXene/CNF复合气凝胶的制备及其湿敏性能研究 |
| Preparation and Humidity Sensing Properties of MXene/CNF Composite Aerogels |
| 收稿日期：2024-01-25 |
| DOI：10.11980/j.issn.0254-508X.2024.08.001 |
| 关键词: CNF MXene 液氮定向冷冻 气凝胶 湿度传感器 |
| Key Words:CNF MXene liquid nitrogen directional freezing aerogel humidity sensor |
| 基金项目:国家自然科学基金项目（22308333）； 浙江省“尖兵”“领雁”科技计划项目（2022C01066）。 |
| 作者 | 单位 | 邮编 | | 沈湘凌 | 浙江科技大学环境与资源学院,浙江杭州,310023 | 310023 | | 陈广杰 | 浙江科技大学环境与资源学院,浙江杭州,310023 | 310023 | | 郭大亮 | 浙江科技大学环境与资源学院,浙江杭州,310023 | 310023 | | 李静 | 浙江科技大学环境与资源学院,浙江杭州,310023 | 310023 | | 童欣 | 浙江科技大学环境与资源学院,浙江杭州,310023 | 310023 |
|
| 摘要点击次数: 3420 |
| 全文下载次数: 2767 |
| 摘要:本研究将新型二维过渡金属碳氮材料（MXene）与纤维素纳米纤维（CNF）复合，通过液氮定向和非定向预冷冻方法，冷冻干燥后制备4种不同MXene/CNF复合气凝胶，探究加入不同类型CNF、MXene和采用不同液氮预冷冻方法对复合气凝胶形貌结构的影响。结果表明，定向单层MXene/TOCNF复合气凝胶形貌最为优异；对其制备的湿度传感器在相对湿度11%~97%的条件下进行了湿敏测试，发现在MXene质量分数10%、相对湿度97%的条件下，传感器响应值增大了3倍，说明传感器对于高湿度更为敏感，且该传感器在14天内基本稳定。 |
| Abstract:In this study， the novel two-dimensional transition metal carbon and nitrogen material （MXene） was composited with cellulose nanofibers （CNF）， and four different kinds of CNF composite aerogel sensors were prepared after freeze-drying by the liquid nitrogen directional and non-directional pre-freezing methods. The impacts of various types of CNF and MXene， with different liquid nitrogen pre-freezing methods on the morphology and structure of the MXene/CNF composite aerogels were investigated. The results showed that the oriented monolayer MXene/TOCNF composite aerogel had the most excellent morphology. Additionally， the humidity sensitivity test was conducted at relative humidity levels ranging from 11%~97%. The results revealed a three times of increase in response value at relative humidity of 97% with MXene dosage of 10%， indicating superior sensitive of the sensor to high humidity. Furthermore， the sensors demonstrated overall stablility within 14 days. |